Species	Product name	Product name	Vulcanization method			Operating temperature	Recommended use ratio	Product Features
			Molded	Squeeze out	Calender
Platinum Vulcanization Agent A	TC-A	Transparent gel	●	●	●	Molding temperature80℃-170℃ Calendering temperature110℃-170℃ Extrusion temperature200℃-400℃	0.1%-0.5%	High activity at low temperature, suitable for low temperature forming thin products.
	TC-AH	Transparent gel	●	●	●		0.1%-0.5%	High content and low addition ratio.
	TC-25A	Transparent gel	●	●	●		0.3%-1.0%	Wide application range and low cost.
	TC-50AH	Transparent gel	●	●	●		0.2%-1.0%	The addition ratio is moderate and easy to add.
	TC-AY	Transparent gel	●	●	●		0.2%-1.0%	Good stability at low temperature, suitable for high temperature molding thick products.
Platinum sulfide B agent	TC-BF1&TC-BF2	White powder	●	●		Molding temperature80℃-170℃ Calendering temperature110℃-170℃ Extrusion temperature200℃-400℃	0.6%-1.0%	High crosslinkability, stable product hardness, suitable for fumed rubber extrusion and molding.
	TC-BF3	White powder	●	●			0.5%-1.0%	Long waiting time, high tear strength of the product, moderate gas phase glue extrusion and molding, cold shrinkable casing glue is the first choice.
	BF-4&BF-7	White powder		●			0.5%-1.0%	Fast curing speed, suitable for precipitation rubber extrusion.
	BF-6	White powder	●	●			0.5%-1.0%	High crosslinkability, especially suitable for high tear resistance adhesives.
	TC-BF3-4	White powder	●				0.5%-1.0%	Long waiting time, suitable for high temperature molded products.
	TC-B1	Transparent gel	●		●		0.8%-2.0%	Long feeding time and good cross-linking.
	TC-B2	Translucent gel	●	●	●		0.8%-2.0%	Long strip time, good cross-linking, thick molded products are preferred.
	TC-B4&TC-B7	Transparent gel	●	●	●		0.8%-2.0%	Easy to add and cost-effective for calendered products.
	TC-B9	Translucent gel	●	●	●		0.8%-2.0%	Shinetsu 25B subsection.
One-component platinum curing agent	ABF1	White powder	●			Temperature120℃-170℃	0.6%-1.0%	Suitable for molded products, long waiting time.
	ABF2	White powder		●		Temperature200℃-400℃	0.6%-1.0%	适合高透明、高抗撕胶挤出。
	ABF3	White powder		●		Temperature200℃-400℃	0.6%-1.0%	It has a wide range of applications, and can be extruded by precipitation glue and gas phase glue.
	ABF3-1	White powder		●		Temperature200℃-400℃	0.6%-1.0%	It has a wide range of applications, and can be extruded by precipitation glue and gas phase glue, and has a long waiting time.
	ABF4-1	White powder		●		Temperature200℃-400℃	0.6%-1.0%	Suitable for precipitation rubber extrusion, long waiting time and high cost performance.
	ABF5	White powder		●		Temperature200℃-400℃	0.6%-1.0%	Special for LED light bar, strong cross-linking, dry and dry surface.
	AB1	Transparent gel	●			Temperature120℃-170℃	1.0%-2.0%	Long storage time at room temperature, suitable for molded products with increased productivity.

Vulcanization molding methods are available: hydraulic vulcanization molding and dieless extrusion calendering vulcanization molding.
Use ratio:TC-A,TC-25A,TC-AH 0.3-1.0% 0.3-1.0% Depend on product needs
TC-B1,TC-B2,TC-B3，TC-B4,TC-B5,TC-B6 0.6-2.0% Depend on product needs
TC-BF1,TC-BF2,TC-BF3,TC-BF4,TC-BF5,TC-BF6,TC-BFP 0.3- 1.0%Depend on product needs
 
The platinum two-component mixing method:
1. Put the silica gel in a rubber mixing machine and mix until it softens. Additives such as colorants can be added during this process.
2. After the softened rubber material silica gel and agent B are evenly mixed, let it cool down.
3. Take agent A and add it to the silica gel that has been mixed with agent B several times in batches, and mix evenly.
4. It can be used for forming operation after being allowed to cool down.
During the mixing process, try to keep the temperature of the rubber mixer roll not exceeding 35°C. It is recommended that the mixer use chilled water circulation when the temperature is high, and measures such as air conditioning to control the ambient temperature should be used to reduce the mixing temperature.

1. It is forbidden to add nitrogen, phosphorus, sulfur, lead, cadmium, polyvinyl, polyethynyl, etc., because the above substances can poison platinum and fail to achieve the purpose of crosslinking.
2. Certain organic silica gel pigments can also cause platinum poisoning and invalidation and cannot be used. Therefore, when choosing platinum vulcanizing agent for production, it must be tested and confirmed before use before unit feeding.
3. After mixing the colloid with platinum vulcanizing agent, it is recommended to vulcanize and form within 4 hours to 8 hours to prevent crosslinking at room temperature. If you need to extend the storage time, you can add a little delay agent. (Our model FM-10)
4. When there is hydrogen-containing silicone oil in the silica gel, mixing Agent A separately will cause the rubber compound to die.
5. When using different types of silica gel, the proportions of A and B added are different. If you have any questions, please call our sales staff for consultation

TC-A, TC-AH, TC-25A transparent gel, iron can packaging, 1Kg/can 10Kg/carton.
TC-B1, TC-B2, TC-B3, TC-B4, TC-B5, TC-B6 transparent gel, packed in plastic cans, 1Kg/can 10Kg/carton.
TC-BF1, TC-BF2, TC-BF3, TC-BF4, TC-BF5, TC-BF6, TC-BFP white powder, plastic tank packaging, 5Kg/barrel

1. Avoid high temperature, direct sunlight, acidic substances, metal oxides, amine substances and flammable materials. They should be stored in a cool and dry place indoors, preferably at 25°C, not refrigerated.
2. The product is non-dangerous and can be transported as general chemicals.
Shelf life
6 months shelf life
The above information is for reference only. If you have any questions, please contact us.