Product number |
Solvent type |
Dilution |
Diluent |
Cycle |
Use the program |
Maximum temperature |
|
TC-615 |
N/A |
At the beginning, it will be diluted with water in a ratio of 1:4, after the mold is fixed with a layer of release agent, it can be diluted in a ratio of 1:10 |
Water |
2~3 molds can be demolded each time |
1. Clean the mold
2. Heating the mold to make the mold reach 150℃
3. Coat a thin layer on the mold and reheat
4. Steps 2 and 3 are executed four times in succession until release agent is produced
5. Demoulding (can increase gloss)
|
175℃ |
TC-615 is a concentrated liquid, which can usually be diluted with water before use. At the beginning, it is recommended to use this product and water at a ratio of 1:4-~1:10. Due to different mold materials, the mold surface roughness is different. The amount of coating and spraying times required for the development of solid release molds also vary with different molds (recommended spraying times 2~5) until After a layer of PTFE film has been fixed on the mold, it can be diluted with a higher proportion of water to achieve an excellent release effect. Although TC-615 is a stable emulsifying release agent, precipitation will still occur. Therefore, it is recommended to mix and shake well before use, and shake regularly before use or after dilution. In order to achieve the best results, the release agent must be applied to a clean mold surface. The mold surface must not be stained with grease, wax or dust, and all previous residual release agents of other brands must be removed. The method of using this product is spraying, dipping or brushing. In order to let the water volatilize quickly and achieve the desired effect, the mold needs to be preheated to above 100°C. If TC-615 is used for anti-sticking, the glue should be used. When there is residual temperature, apply the anti-sticking agent and dry naturally. If the rubber material has fallen to room temperature, the anti-sticking agent applied on it needs to be dried separately. Performance characteristics
1. Release coating
Will not be transferred to the finished product
Keep the mold surface clean
Form a colorless, dry and non-oily film coating
Excellent chemical stability
Good secondary processing
No trace of rubber flow
With multiple release effects
It also has a fairly superior demolding effect for silicone products
2. Anti-sticking agent for raw rubber
Form a colorless, dry and non-oily film coating
Will not be transferred to the finished product
There will be no dust problems like mica powder, talcum powder, etc.
Economical
Excellent chemical stability
1. Do not refrigerate this product
2. If the eyes come into contact with this product accidentally, rinse with water to relieve the stinging sensation, and avoid prolonged contact with the skin.
20KG/barrel
Store at room temperature, the shelf life is 12 months